Aluminum vs Fiberglass landing gear - Pro's and cons.



 
 
Thread Tools Display Modes
  #1  
Old November 24th 03, 05:31 AM
Bart Hull
external usenet poster
 
Posts: n/a
Default Aluminum vs Fiberglass landing gear - Pro's and cons.

I'm in the process of building a Team Tango (similar to a Glasair IIFG) and have
a few thoughts about the landing gear. The earlier kits had fiberglass "legs"
and the newer kits have aluminum legs.

I flew in a Tango with the aluminum gear and it seemed quite harsh on landing. I
know aluminum gear doesn't have problems with heat transferred from the brakes
or axle getting things too hot and that the gear can be "gun drilled" to have
they hydraulic lines inside the gear itself with just a small connector hose
from the gear leg to the brake caliper.

Does the aluminum gear have less ability to absorb shock?

Does the fiberglass or aluminum gear take a "set" after awhile setting on a ramp?

Problems with brake lines on fiberglass gear? on aluminum gear.

How do you match the appropriate gear to the airplanes weight?

Can aluminum gear be had in a "aerodynamic" tear drop shape or just a
bent bar.

Any other suggestions would be appreciated. ( pertaining to the gear )

--
Bart D. Hull

Tempe, Arizona

Check
http://www.inficad.com/~bdhull/engine.html
for my Subaru Engine Conversion
Check http://www.inficad.com/~bdhull/fuselage.html
for Tango II I'm building.




Ads
  #2  
Old November 24th 03, 05:54 AM
Del Rawlins
external usenet poster
 
Posts: n/a
Default

We heard you the first time....

On 23 Nov 2003 07:31 PM, Bart Hull posted the following:
I'm in the process of building a Team Tango (similar to a Glasair IIFG)
and have a few thoughts about the landing gear. The earlier kits had
fiberglass "legs" and the newer kits have aluminum legs.

I flew in a Tango with the aluminum gear and it seemed quite harsh on
landing. I know aluminum gear doesn't have problems with heat
transferred from the brakes or axle getting things too hot and that
the gear can be "gun drilled" to have they hydraulic lines inside the
gear itself with just a small connector hose from the gear leg to the
brake caliper.

Does the aluminum gear have less ability to absorb shock?

Does the fiberglass or aluminum gear take a "set" after awhile setting
on a ramp?

Problems with brake lines on fiberglass gear? on aluminum gear.

How do you match the appropriate gear to the airplanes weight?

Can aluminum gear be had in a "aerodynamic" tear drop shape or just a
bent bar.

Any other suggestions would be appreciated. ( pertaining to the gear )

--
----------------------------------------------------
Del Rawlins-
Remove _kills_spammers_ to reply via email.
Unofficial Bearhawk FAQ website:
http://www.rawlinsbrothers.org/bhfaq/
  #3  
Old November 24th 03, 06:23 AM
Bart D. Hull
external usenet poster
 
Posts: n/a
Default

Sorry, but it never showed up when I looked for it after I sent it (until now.)

Bart
--
Bart D. Hull

Tempe, Arizona

Check
http://www.inficad.com/~bdhull/engine.html
for my Subaru Engine Conversion
Check http://www.inficad.com/~bdhull/fuselage.html
for Tango II I'm building.

Del Rawlins wrote:

We heard you the first time....

On 23 Nov 2003 07:31 PM, Bart Hull posted the following:

I'm in the process of building a Team Tango (similar to a Glasair IIFG)
and have a few thoughts about the landing gear. The earlier kits had
fiberglass "legs" and the newer kits have aluminum legs.

I flew in a Tango with the aluminum gear and it seemed quite harsh on
landing. I know aluminum gear doesn't have problems with heat
transferred from the brakes or axle getting things too hot and that
the gear can be "gun drilled" to have they hydraulic lines inside the
gear itself with just a small connector hose from the gear leg to the
brake caliper.

Does the aluminum gear have less ability to absorb shock?

Does the fiberglass or aluminum gear take a "set" after awhile setting
on a ramp?

Problems with brake lines on fiberglass gear? on aluminum gear.

How do you match the appropriate gear to the airplanes weight?

Can aluminum gear be had in a "aerodynamic" tear drop shape or just a
bent bar.

Any other suggestions would be appreciated. ( pertaining to the gear )



 




Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

vB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump

Similar Threads
Thread Thread Starter Forum Replies Last Post
Aluminum vs Fiberglass landing gear - Pro's and cons. Bart Hull Home Built 0 November 24th 03 04:52 AM
Aluminum vs Fiberglass landing gear - Pro's and cons. Bart D. Hull Home Built 0 November 22nd 03 07:24 AM


All times are GMT +1. The time now is 03:56 PM.


Powered by vBulletin® Version 3.6.4
Copyright ©2000 - 2018, Jelsoft Enterprises Ltd.
Copyright 2004-2018 AviationBanter.
The comments are property of their posters.